Characterization 410 Stainless Steel by Vacuum Tempering Process

( Vol-3,Issue-5,May 2017 )

Author(s): Dr.Ram.Subbiah, B.Uday Babu, C.Dinesh Reddy, D.Praharsha, E.Ajay Babu, Dr.R.Rajavel



Total View : 1171
Downloads : 164
Page No: 619-621
ijaems crossref doiDOI: 10.24001/ijaems.3.5.36

Keywords:

vacuum tempering, brittleness, wear resistance, metallographic results.

Abstract:

It has been reported that low-temperature vacuum tempering of 410 stainless steel hard layer improving wear resistance and hardness. Grade 410 stainless steel being a hardened material were modified by low temperature tempering process. By the process of tempering, brittleness on the stainless steel material will be reduced and ductility will be promoted. The microstructure, surface hardness and erosion-corrosion resistance were systematically evaluated. Vacuum tempering is done at low temperature of 430℃ can form a hardened layer, and with the treated time prolong, the thickness of the layer increased. The stainless specimens were vacuum tempered for 30 minutes, 60 minutes and 120 minutes. Wear tests were conducted with the help of pin on disc apparatus. The output results were determined with various metallographic tests like scanning electron microscope and optical microscope results.